几篇电解液新型添加剂文献总结.ppt

《几篇电解液新型添加剂文献总结.ppt》由会员分享，可在线阅读，更多相关《几篇电解液新型添加剂文献总结.ppt（28页珍藏版）》请在三一办公上搜索。

1、Tris(1,1,1,3,3,3-hexafluoroisopropyl)phosphate三（六氟异丙基）磷酸酯CAS：66489-68-7,5V级高电压电解液添加剂，添加量为1wt%与MCMB具有良好的相容性，与PC共用可防止PC的共嵌分解,Electrolyte Additive in Support of 5 V Li Ion Chemistr徐康Journal of The Electrochemical Society,158（3）A337-A342（2011）,Phosphate and phosphazene electrolyte additives for Li-ion b

2、atteriesMeet.Abstr.2012,Volume MA2012-01,Issue 6,Pages 334.,Tris(hexafluoro-isopropyl)phosphate was first observed to extend the cycling life of a full 4.7V Li-ion cell using a LiNi0.5Mn1.5O4cathode and a commercial graphite anode.This particular heavily fluorinated phosphate was also usedsuccessful

3、ly to allow extended(500 cycles)useful cycling of a 4.8V LiCoPO4cathode vs.lithium,4-(perfluorohexyl)-1,3-dioxolan-2-one,3,3,3-Trifluoropropylene carbonate三氟代碳酸丙烯酯CAS：167951-80-6,4-(perfluorobutyl)-1,3-dioxolan-2-one,4-(perfluorooctyl)-1,3-dioxolan-2-onePFO-EC,Perfluoroalkyl-substituted ethylene car

4、bonates:Novel electrolyte additives for high-voltage lithium-ion batteriesJournal of Power Sources 246(2014)184-191,4-全氟辛基碳酸乙烯酯（PFO-EC），正极4.3V氧化分解成膜，降低正极cycles阻抗；负极与EC分解产物聚合形成溶解性小的SEI膜。,PFO-EC在(EC:EMC=3:7，1.2MLiPF6）溶解性较差，最大浓度为2wt%,而其他溶解度为5wt%。推测PFO-EC的分解产物在电解液中的溶解性较低，从而成膜稳定性高。,(EC:EMC=3:7，1.2M LiPF6

5、，0.5wtPFO-EC,Li1.2Ni0.15Mn0.55Co0.1O2-石墨（2.2-4.1,3cycles；C/3 2.2-4.6 200cycles）容量保持率为66%（172mAh/g）。,Trimethyl phosphite亚磷酸三甲酯 CAS：121-45-9,适用于富锂高电压正极，可正极成膜，提高正极材料的电化学性能和热稳定性；含量不宜超过2wt%。,Trimethyl phosphite as an electrolyte additive for high-voltagelithium-ion batteries using lithium-rich layered ox

6、ide cathodeJournal of Power Sources 240(2013)471-475,Li1.2Mn0.54Ni0.13Co0.13O2：，0.1C首次充电；，0.5C 100cycles,189.5mAh/g(81.3%)；150mAh/g(5C)、90mAh/g(10C),Tris(pentafluorophenyl)phosphine三(五氟苯基)膦CAS：1259-35-4,高电压添加剂，cycles Ok，倍率不佳；用量为0.5wt%较宜，1wt%性能不佳。,Tris(pentafluorophenyl)phosphine:An electrolyte addit

7、ive for high voltage Li-ion batteriesElectrochemistry Communications 18(2012)123126,Li/LiNi0.5Mn1.5O4,（1M LiPF6，EC：DMC：DEC=1:1:1，0.5wt%TPFPP）：3.5V-4.9V,0.2C 55cycles,106.9mAh/g(85.0%)。但倍率性能仍不佳，与正极材料电导率差有关，可通过碳包覆改善,Tris(pentafluorophenyl)borane三(五氟苯基)硼烷TPFPBCAS：1109-15-5,三(五氟苯基)硼烷(TPFPB),作为阴离子受体，参与负极

8、成膜并溶剂LiF，提高SEI的导Li+，从而提高电池的电化学性能，对正极没有影响，用量3%为宜（1%），过多则促进锂盐的分解且增大界面阻抗，降低电池的性能。,Tris(pentafluorophenyl)Borane as an Additive to Improve the Power Capabilities of Lithium-Ion BatteriesJournal of The Electrochemical Society,153(6),A1221-A1225(2006),N-(Triphenylphosphoranylidene)aniline四苯基氨化膦CAS：2325-27

9、-1,添加0.2wt%TPPA，可优先溶剂在LCO表面成膜，阻止电解液及锂盐的分解，提高其工作电压到4.4V，且对负极MCMB没有影响。,N-(triphenylphosphoranylidene)aniline as a novel electrolyte additive for high voltage LiCoO2 operations in lithium ion batteries,RF：EC:EMC:DMC=1:1:1,1M LiPF6EL：EC:EMC:DMC=1:1:1,1M LiPF6，0.2wt%TPPA,ECS Electrochemistry Letters,1(3)

10、A50-A53(2012),Methylene methanedisulfonate甲烷二磺酸亚甲酯CAS：99591-74-9,MMDS可提高LNMC/C电池4.4V的cycles性能，100cycles（70.7%94.1%），但对4.2V电池改善效果不明显。MMDS高压下可在正极分解成膜，降低LiF的含量，提高界面导锂新能，同时抑制LiPF6及电解液在正极表面的分解。,1,1,1,3,3,3-Hexafluoroisopropyl acrylate 1,1,1,3,3,3-六氟异丙基丙烯酸酯CAS：2160-89-6,2-PHENYL-1,3,2-DIOXABORINANE苯基硼酸1,3-丙二醇酯CAS：4406-77-3,2-(1,3,2-DIOXABORINAN-2-YL)BENZONITRILE2-氰基苯硼酸 1,3-丙二醇酯CAS：172732-52-4,Ethyl isobutyl sulfoneCAS:34008-93-0,Li,LiFAP(三（五氟乙基）三氟磷酸锂)相对LiPF6对水不敏感，热稳定性佳，可替代LiPF6在高电压中应用；（1M LiFAP，EC：DMC=1:1，1.6wtFEC，2wt%丁二酸酐），C/10，25cycles，容量保持率70%(without additive)和87%(with additive)。但电池自放电率高。,