1、AS 17892003Accessed by ISONET - CHINA STATE BUREAU OF TECHNICAL SUPERVIS on 03 Apr 2007AS 1789Australian StandardElectroplated zinc (electrogalvanized)coatings on ferrous articles(batch process)Accessed by ISONET - CHINA STATE BUREAU OF TECHNICAL SUPERVIS on 03 Apr 2007This Australian Standard was p

2、repared by Committee MT-009, Metal Finishing. It wasapprovedonbehalfoftheCouncilofStandardsAustraliaon8 August 2003 and published on 11 September 2003.The following are represented on Committee MT-009: Australian Chamber of Commerce and IndustryAustralian Industry GroupAustralian Institute of Metal

3、FinishingAustralian Paint Manufacturers Association Bureau of Steel Manufacturers of Australia Department of DefenceGalvanizers Association of AustraliaInstitute of Materials Engineering AustralasiaPowder Coaters AssociationThe Royal Australian Chemical InstituteSociety of Automotive EngineersAustra

4、lasiaTelstra CorporationKeeping Standards up-to-dateStandards are living documents which reflect progress in science, technology and systems. To maintain their currency, all Standards are periodically reviewed, and new editions are published. Between editions, amendments may be issued. Standards may

5、 also be withdrawn. It is important that readers assure themselves they are using a current Standard, which should include any amendments which may have been published since the Standard was purchased.Detailed information about Standards can be found by visiting the Standards Australia web site at .

6、au and looking up the relevant Standard in the on-line catalogue.Alternatively, the printed Catalogue provides information current at 1 January each year, and the monthly magazine, The Global Standard, has a full listing of revisions and amendments published each month.We also welcome suggestions fo

7、r improvement in our Standards, and especially encourage readers to notify us immediately of any apparent inaccuracies or ambiguities. Contact us via email at mail.au, or write to the Chief Executive, Standards Australia International Ltd, GPO Box 5420, Sydney, NSW2001.This Standard was issued in dr

8、aft form for comment as DR 03202.AS 17892003Accessed by ISONET - CHINA STATE BUREAU OF TECHNICAL SUPERVIS on 03 Apr 2007Australian StandardElectroplated zinc (electrogalvanized)coatings on ferrous articles(batch process)Originated as AS K1441963, AS CK81963 and AS CK101965. Previous editions AS 1789

9、1984 and AS 17911986.AS 17891984 and AS 17911986 revised, amalgamated and redesignated as AS 17892003.COPYRIGHT Standards Australia InternationalAll rights are reserved. No part of this work may be reproduced or copied in any form or by any means, electronic or mechanical, including photocopying, wi

10、thout the written permission of the publisher.Published by Standards Australia International LtdGPO Box 5420, Sydney, NSW 2001, AustraliaISBN 0 7337 5486 4Accessed by ISONET - CHINA STATE BUREAU OF TECHNICAL SUPERVIS on 03 Apr 2007PREFACEThis Standard was prepared by the Australian members of the Jo

11、int Standards Australia/New Zealand Committee MT-009, Metal Finishing to supersede AS 17891984, Electroplated coatingsZinc on iron or steel and AS 17911986, Chromate conversion coatingsZinc and cadmium. After consultation with stakeholders in both countries, Standards Australia and Standards New Zea

12、land decided to develop this Standard as an Australian Standard rather than as an Australian/New Zealand Standard.The objective of this Standard is to specify requirements for the electroplating of zinc (electrogalvanizing) and for the application of supplementary chromate conversion coatings, on ir

13、on and steel articles by batch processing, as opposed to continuous processing. For this purpose the technical content of AS 1791, Chromate conversion coatingsZinc and cadmium, has been incorporated into this revision of AS 1789. Notwithstanding, passivation systems other than chromate are permissib

14、le.Some manufacturers which zinc-electroplate dedicated articles on a large scale, using specialized, purpose-built facilities, prefer to describe their products as having been electrogalvanized. Since the latter term is technically acceptable and is favoured by a significant section of the marketpl

15、ace, it has been incorporated into this revision of the Standard as a valid alternative term to electroplated zinc.The content of this Standard relates to electrodeposition of zinc by the batch process. For the continuous process, reference should be made to AS 4750, Electrogalvanized (zinc) coating

16、s on ferrous hollow and open sections. Hollow and open sections are, in general, semi-finished products, rather than commodities for use without significant further working or fabrication, which this Standard (i.e. AS 1789) covers.This Standard specifies a range of electroplated zinc coatings for th

17、e protection of iron and steel against corrosion under various service conditions. It is a modification of ISO 2081:1986, Metallic coatingsElectroplated coatings of zinc on iron or steel and incorporates parts of ISO 4520, Chromate conversion coatings on electroplated zinc and cadmium coatings.It is

18、 essential that purchasers state the coating classification code when placing their zinc coating orders with electroplaters. Likewise, manufacturers are required to state the coating classification code, when offering zinc plated (electrogalvanized) commodities for sale on the open market.The terms

19、normative and informative have been used in this Standard to define the application of the Appendix to which they apply. A normative Appendix is an integral part of a Standard, whereas an informative Appendix is only for information and guidance.Statements expressed in mandatory terms in footnotes t

20、o tables are deemed to be requirements of this Standard.AS 1789200331Accessed by ISONET - CHINA STATE BUREAU OF TECHNICAL SUPERVIS on 03 Apr 2007CONTENTSPageFOREWORD . 41SCOPE .5 2REFERENCE DOCUMENTS . 53DEFINITIONS . 64BASIS METAL. 65COATING SYSTEM . 76COATING CLASSIFICATION CODE. 87HEAT TREATMENT

21、. 98ZINC WHISKER GROWTH . 99ZINC COATING REQUIREMENTS. 910TEST METHODS FOR ZINC COATINGS . 1011CHROMATE CONVERSION COATINGS . 1012REQUIREMENTS AND TESTS FOR CHROMATE CONVERSION COATINGS. 1113CONFORMANCE . 1114IDENTIFICATION . 11APPENDICESAINFORMATION TO BE SUPPLIED TO THE ELECTROPLATER. 13BFACTORS T

22、HAT AFFECT THE CORROSION OF ZINC COATED ARTICLES . 14CMAINTENANCE OF ZINC-PLATED ARTICLES. 20DPRETREATMENT OF IRON OR STEEL TO REDUCE THE RISK OFHYDROGEN EMBRITTLEMENT . 21EPOST-COATING TREATMENTS OF IRON OR STEEL TO REDUCE THE RISKOF HYDROGEN EMBRITTLEMENT . 24FRENOVATION OF DAMAGED AREAS . 28GTEST

23、 METHODS FOR CHROMATE CONVERSION COATINGSON ZINC COATINGS . 29Accessed by ISONET - CHINA STATE BUREAU OF TECHNICAL SUPERVIS on 03 Apr 2007FOREWORDThis Standard specifies requirements for a range of thicknesses of zinc coatings to be applied to ferrous articles as protection against corrosion, but do

24、es not specify the surface condition, nor other aspects, of the basis metal.The thickness of the zinc coating to be applied to the ferrous articles should be chosen by the purchaser, or by the manufacturer if the articles are for sale as a general commodity, to provide sufficient corrosion protectio

25、n for the expected or design life of the articles under the environmental conditions to which they are to be exposed.Electroplated zinc coatings are normally chromate treated to retard the formation of corrosion products on surfaces exposed to corrosive atmospheres. The type of chromate coating to b

26、e applied should be appropriate for the expected exposure environment.Since chromate conversion coatings give additional protection against corrosion, they may only be omitted at the specific request of the purchaser. Zinc-plated articles intended to be painted may require a specific treatment, such

27、 as phosphating, to provide good paint adhesion. Other passivation systems may be substituted by agreement between interested parties.Zinc-plated items are subject to attack by certain organic materials that release reactive vapours, such as cardboard, wood and certain electrical insulating material

28、s. Cognizance should be taken of this when items are packed, stored or transported.Accessed by ISONET - CHINA STATE BUREAU OF TECHNICAL SUPERVIS on 03 Apr 2007STANDARDS AUSTRALIAAustralian StandardElectroplated zinc (electrogalvanized) coatings on ferrous articles(batch process)1 SCOPEThis Standard

29、specifies requirements for electroplated zinc coatings (or electrogalvanized coatings, see Note 1) on iron and steel articles by the batch process, except for coatings applied to(a) sheet, strip or wire in the unfabricated form (see Note 2); (b)threaded fasteners (see Note 3); and(c) close-coiled sp

30、rings.The Standard also specifies supplementary coatings, specifically chromate and other passivation systems, and makes provision for optional organic/inorganic coatings. It includes requirements for heat treatment, both before and after electroplating.Appendix A sets out information to be supplied

31、 by the purchaser to the electroplater, or electrogalvanizer.NOTES:1The term electrogalvanize, as well as its derivatives, is a technically acceptable alternative to zinc electroplate, provided that it is not abbreviated to galvanize, since the latter is the traditional contraction for hot-dip galva

32、nize.2Electrogalvanized coatings for strip are covered by AS 4750, while those for wire are incorporated in AS/NZS 4534.3The coating thickness that can be applied to threaded components may be limited by dimensional requirements, including class or fit. For guidance, attention is drawn to AS 1897, w

33、hich specifies the maximum thickness that can be applied to standard threads4Specifications for electroplated zinc alloys are beyond the scope of this Standard.5Appendix B provides general information on factors that affect the corrosion of zinc-coated articles with further information being provide

34、d in AS/NZS 2312.6Recommendations on maintenance and repair procedures for zinc-coated articles are given inAppendix C2 REFERENCE DOCUMENTSThe following documents are referred to in this Standard: AS1627Metal finishingPreparation and pretreatment of surfaces1627.0Method 0: Method selection guide1897

35、Electroplated coatings on threaded components (metric coarse series)2331Methods of test for metallic and related coatings2331.1.1Method 1.1: Local thickness testsMicrographic examination of cross-sections2331.1.2Method 1.2: Local thickness tests Coulometric method2331.1.3Method 1.3: Local thickness

36、tests Magnetic method2331.2.1Method 2.1: Tests for average coating mass per unit area or for thickness Dissolution methodsStrip and weigh and analytical2331.3.1Method 3.1: Corrosion and related property testsNeutral salt spray (NSS) test.au Standards AustraliaAccessed by ISONET - CHINA STATE BUREAU

37、OF TECHNICAL SUPERVIS on 03 Apr 2007AS2331.3.8Method 3.8: Corrosion and related property testsHumidity test24 h cycle, damp heat2331.4.1Method 4.1: Physical testsQualitative adhesion tests2483Metal finishingRecommended sampling plans for the inspection and testing of coatings (ISO 4519:1980, MOD)429

38、1Mechanical properties of fasteners made of carbon steel and alloy steel4291.1Part 1: Bolts, screws and studs4750Electrogalvanized (zinc) coatings on ferrous hollow and open sectionsAS/NZS2312Guide to the protection of structural steel against atmospheric corrosion by the use of protective coatings3

39、750Paints for steel structures3750.9Part 9: Organic zinc-rich primer4534Zinc and zinc/aluminium-alloy coatings on steel wire4680Hot-dip galvanized (zinc) coatings on fabricated ferrous articlesISO4518Metallic coatingsMeasurement of coating thicknessProfilometric method9223Corrosion of metals and all

40、oysCorrosivity of atmospheresClassification12686Metallic and other inorganic coatingsAutomated controlled shot-peening of metallic articles prior to nickel, autocatalytic nickel or chromium plating, or as a final finish3 DEFINITIONSFor the purpose of this Standard, the definitions below apply.3.1 Local thicknessThe mean of the thickness measurements, of which a specified number is made within a reference area.3.2 Minimum local thicknessThe lowest value of the local thickness found on t