400万吨冷轧板带钢车间设计毕业设计论文.doc

400万吨冷轧板带钢车间设计摘要本次设计是参考宝钢冷轧厂2030生产线设计而成，年产量为400万吨，典型产品为Q345冷轧薄板带钢，产品规格1.21280mm。主要设备机组包括连续酸洗五机架连轧机组、罩式退火炉机组、单机架四辊平整机组、连续式退火炉机组、连续式热镀锌机组、连续电镀锌机组、涂层机组、剪切机组和重卷包装机组。设计阐述了冷轧带钢的生产工艺特点、应用、发展状况并简要介绍冷轧薄板带钢的生产工艺流程，进而设计出以Q345为代表的冷轧产品、特深冲产品、热镀锌产品、电镀锌产品和涂层产品。根据年产能力制定了轧制制度，计算了轧制力，对轧辊强度，电机能力，车间年产量进行了校核。同时还介绍了各项经济技术指标。最后论述了冷轧能耗数学模型以及数学模型在轧钢生产中的应用等方面的内容。关键词：冷轧带钢；轧制工艺；轧制制度；校核；冷轧能耗模型 Workshop design for a cold-rolled strip plant with an annual yield of 4 million tonsABSTRACTReferring to Baosteel 2030mm workshop, a plant for typical product of Q345, 1.21280mm with annual yield of 4 million tons was designed. Major facilities include continuous acidwashing and five frame continuous rolling crew, hood-type annealing furnace, single frame skin rolling unit with four rolls, continuous annealing furnace, continuous hot galvanizing unit, coating unit, shearing unit, rewinding and packing unit. The design described processing features, application, development of the cold-rolled strip steel, and briefly introduced production technology, designed cold-rolled products, super deep punched products, hot galvanized products, electrogalvanized products, and coated products. According to the producing capacity, rolling schedule was determined, rolling force was calculated, the roll strength, motor capacity, and the annual yield of the workshop were checked, and the economic and technical norms were introduced. At the end, the typical energy-consumption math models for cold rolling and their application in steeling rolling were described.Key words: Cold-rolled steel strip; Rolling process; Rolling system; check; Cold-rolled consumption model目 录摘要IABSTRACTII目 录III1 文献综述11.1冷轧带钢产品的发展、应用及地位11.2 冷轧薄板带钢生产工艺特点11.2.1加工温度低，在轧制中将产生不同程度的加工硬化11.2.2冷轧中要采用工艺冷却和润滑（工艺冷润）11.2.3冷轧中要采用张力轧制11.3 冷轧生产工艺流程11.3.1 酸洗11.3.2 轧制11.3.3 精整11.3.4 镀锌11.3.5 矫直11.3.6 板带钢轧制制度的确定11.4 冷轧薄钢板生产的发展历史11.4.1 国际冷轧发展史11.4.2 我国冷轧发展史11.5 当今现代轧制工艺技术的特点11.5.1大力开发高精度轧制技术11.5.2轧制过程连续化的新进展无头轧制技术11.5.3轧制过程的自动控制和智能控制技术11.5.4深加工技术11.6 几种冷轧薄板带钢轧机设备介绍11.6.1 二辊轧机11.6.2 四辊式冷轧机11.6.3 MKW型轧机21.6.4 二十辊冷轧机21.6.5 特种结构的轧机22 产品方案和金属平衡表的制定22.1 原料及技术要求22.1.1 原料规格22.1.2 原料种类32.1.3 原料技术要求32.2 产品方案42.2.1 冷轧板卷42.2.2 特深冲板卷42.2.3 热镀锌板卷42.2.4 电镀锌板卷42.2.5涂层产品42.3 产品方案表42.3.1 冷轧带钢规格数量分配 (总产量240万吨)42.3.2 特深冲带钢规格数量分配(总产量60万吨)42.3.3 热镀锌带钢规格数量分配(总产量40万吨)42.3.4 电镀锌带钢规格数量分配(总产量32万吨)42.3.5 涂层带钢规格数量分配(总产量28万吨)43 轧制工艺流程及轧制制度的制定43.1 轧制工艺流程图43.2 各部分工艺流程43.2.1 带钢连续加工处理机组43.2.2 酸洗-冷轧联合机组43.2.3 单垛式紧卷罩式退火机组43.2.4 连续热镀锌机组43.2.5 连续电镀锌机组43.2.6 涂层机组43.2.7 薄板横剪机组和包装机组43.2.8 连续辊压成形机组（备选）43.3轧制制度的制定43.3.1 压下规程的制定43.3.2 计算各道轧制压下的步骤说明43.3.3 轧制速度制定43.3.4 辊型制度44 设备的选择44.1 酸洗冷轧联合机组44.2 罩式退火机组44.3 单机架四辊平整机组44.4 连续热镀锌机组44.5 连续电镀锌机组44.6 涂层机组44.7 剪切机组44.8 重卷机组45 轧机生产能力校核45.1 轧辊强度校核45.1.1 轧辊各部分尺寸的确定45.1.2 轧辊强度校核45.2轧机生产能力校核45.2.1 轧机工作图表45.2.2 轧机年生产能力校核45.2.3 轧机平均小时产量45.2.4 车间年产量计算45.3 电机功率校核45.4 咬入角校核46车间平面布置46.1 仓库面积计算46.1.1原料仓库面积46.1.2中间仓库面积46.1.3成品仓库面积46.1.4其它面积46.2 设备间距确定46.2.1轧机机列间的距离46.2.2 轧机到切断设备的距离46.3 车间跨距组成47 各项经济指标47.1概述47.2各项经济技术指标的确定4结 束 语4专题部分4致 谢4参考文献41 文献综述1.1冷轧带钢产品的发展、应用及地位1.2 冷轧薄板带钢生产工艺特点1.2.1加工温度低，在轧制中将产生不同程度的加工硬化1.2.2冷轧中要采用工艺冷却和润滑（工艺冷润）1.2.3冷轧中要采用张力轧制1.2 冷轧薄板带钢产品的发展、应用及重要地位1.3 冷轧生产工艺流程1.3.1 酸洗1.3.2 轧制1.3.3 精整1.3.4 镀锌1.3.5 矫直1.3.6 板带钢轧制制度的确定1.4 冷轧薄钢板生产的发展历史1.4.1 国际冷轧发展史1.4.2 我国冷轧发展史1.5 当今现代轧制工艺技术的特点1.5.1大力开发高精度轧制技术1.5.2轧制过程连续化的新进展无头轧制技术1.5.3轧制过程的自动控制和智能控制技术1.5.4深加工技术1.6 几种冷轧薄板带钢轧机设备介绍1.6.1 二辊轧机1.6.2 四辊式冷轧机1.6.3 MKW型轧机1.6.4 二十辊冷轧机1.6.5 特种结构的轧机 (1) HC轧机的主要优点 (2) HC轧机控制装置2. CVC轧机3. 最新的UPC轧机1.6.4 二十辊冷轧机1.6.5 特种结构的轧机 (1) HC轧机的主要优点 (2) HC轧机控制装置2. CVC轧机3. 最新的UPC轧机2 产品方案和金属平衡表的制定2.1 原料及技术要求2.1.1 原料规格典型产品：Q345, 1.21280mm，年产量为400万吨。本车间所使用的原料为热轧板卷。 厚度(H)：1.55.0毫米；宽度(B)：10002000毫米；原料热轧板卷的规格 内径(r)：800毫米；外径(R)：10002150毫米；卷重(m)：30吨2.1.2 原料种类表2.1 原料钢种普通碳素结构钢优质碳素结构钢低合金碳素结构钢Q205Q23507A1 18Z16MnXt 09MnXt St10 RRSt1430#-45#DL08USt10-USt14K06A115Ti2.1.3 原料技术要求1钢卷不允许有大尺寸的破边和裂边。内部晶粒大小适中、组织均匀，保证轧后产品的质量和性能。2来料不得有扁卷，内圈松3圈，外圈松1圈，层与层间缝隙10mm。3来料侧边的镰刀弯在2m内不应大于6mm；纵切钢带的镰刀弯每2m内不应大于4mm。钢板应切成直角，切斜不得使钢板长度和宽度小于公称尺寸并须保证订货公称尺寸的最小矩形。不能有大尺寸的瓢曲。4. 来料鱼尾的最高和最低差值300mm。头尾尺寸差不能过大，以免影响轧过程和焊接后的牢固性。5来料带钢应卷紧，边缘整齐，内圈无舌头，头部无向上弯起900以上的边缘。6. 带钢表面不应有气泡、结疤、折叠、裂纹、夹杂、压入铁皮等对使用有害的缺陷，侧面不应有分层。7带钢表面不应有超过厚度偏差一半的麻点、凹面、划痕等轻微局部缺陷，但应保证钢带允许的最小厚度。8热轧带钢断面形状呈轻微凸形，中间厚度应比边部厚度大30100微米，不希望出现楔形或其它形状。9热轧带钢不平度要求表2.2 不平度要求公称厚度(mm)测量单位长度(mm)不平度(mm)1.515>1.5412>410100010>10258>25710原料宽度要求表2.3 厚度要求公称宽度(mm)允许偏差(mm)厚度(mm)4.0>4.06.0>6.08.0>8.0160±0.5±0.8±1.0±1.2>160250±1.5±1.0±1.2±1.4>250600±1.0±1.0±1.2±1.4本车间生产的冷轧产品包括冷轧板卷240万吨特深冲板卷60万吨热镀锌板卷40万吨电镀锌板卷32万吨涂层板卷28万吨冷轧钢板80万吨冷轧钢卷160万吨特深冲钢板24万吨特深冲钢卷36万吨热镀锌钢板16万吨热镀锌钢卷24万吨电镀锌钢板12万吨电镀锌钢卷20万吨涂层钢板12万吨涂层钢卷16万吨2.2 产品方案表2.4 冷轧厂产品方案序号名称规格(mm)热处理质量级别产量(t)百分比(%)强度和镀涂量(g·m-2)1冷轧产品厚度：0.53.00宽度：6002000CQDQ24060B=2835Kg/mm22特深冲产品厚度：0.53.00宽度：6002000CQDDQ6015B=2838Kg/mm2；S<24Kg/mm2L=80=30%3热镀锌产品厚度：0.53.00宽度：6001500DQHSSFH401060700；锌层按三点取样；双面镀层；差厚镀层；规则锌花，最小锌花，平整，涂油和钝化4电镀锌产品厚度：1.503.50宽度：<1100DQDDQ328锌层(标准)：0.350 (每面)；单面镀锌：0/100/40；差厚镀层：0.3/2020/30磷化，钝化和表面处理5涂层产品厚度：1.55.0宽度：6001800DQHSS2872.5200m；双面涂层；单面涂层双层，单层和印花注：质量级别：CQ普通商用级；DQ深冲级；DDQ特深冲级；FH全硬级；HSS产品包括固溶型、析出型、烘烤硬化型、双相组织型及TRIP钢等，最高强度级别为340980Mpa。2.2.1 冷轧板卷钢板80万吨，钢卷160万吨钢板规格：长度：30005000mm；宽度：6002000mm；厚度：0.53.0mm；板堆重量：1000kg；单板堆高度：400mm；钢卷规格：宽度：6002000mm；内径：600mm；外径：11002000mm； 卷重：最大32t2.2.2 特深冲板卷钢板24万吨，钢卷36万吨钢板规格：长度：30005000mm；宽度：6002000mm；厚度：0.53.0mm；板堆重量：1000kg；板堆高度：500mm钢卷规格：宽度：6001200mm；内径：600mm；外径：11002000mm；卷重：最大32t2.2.3 热镀锌板卷镀锌层重量：60700g/dm2，其中钢板16万吨，钢卷24万吨钢板规格：长度：30005000mm；宽度：6001800mm；厚度：0.53.0mm；板堆重量：1000kg；板堆高度：600mm钢卷规格：宽度：6001500mm；内径：600mm；外径：11002000mm；卷重：最大32t2.2.4 电镀锌板卷其中钢板12万吨，钢卷20万吨钢板规格：长度：30005000mm；宽度：6001700mm；厚度：1.503.0mm板堆重量：1000kg；板堆高度：600mm钢卷规格：宽度：6001100mm；内径：600mm；外径：11002000mm卷重：最大32t2.2.5涂层产品其中钢板12万吨，钢卷16万吨钢板规格：长度：30005000mm；宽度：6001700mm；厚度：1.503.0mm板堆重量：1000kg；板堆高度：700mm钢卷规格：宽度：6001100mm；内径：600mm；外径：11002000mm卷重：最大32t2.3 产品方案表按上述产品分配计划制定金属平衡表，如下：表2.5金属平衡表产品名称年产量(万吨)成材率(%)溶损(%)几何损失(%)工艺损失(%)年需坯料量(万吨)冷轧板8097.00.51.70.882.54冷轧卷16097.90.51.10.5163.43特深冲板2497.60.51.10.624.59特深冲卷3697.70.51.10.736.85热镀锌板1696.70.52.01.016.55热镀锌卷2497.40.51.30.824.64电镀锌卷2096.90.51.70.920.64电镀锌板1296.90.51.70.912.38涂层板1296.60.51.91.012.42涂层卷1696.50.52.01.016.58总计400410.62表中：溶损包括酸洗损失；几何损失包括切头尾，切定尺，切变等；工艺损失包括：轧废根据金属平衡表计算得所需原料为410.62万吨。2.3.1 冷轧带钢规格数量分配 (总产量240万吨)表2.6冷轧带钢规格数量分配表 万吨/年带钢厚度(mm)所占比例带钢宽度（mm）所占比例600900900150015002000合计万吨%万吨%万吨%万吨%0.50.820.565.1420.125.0318.084.5258.7614.690.81.220.205.0520.125.0319.564.8959.8814.971.22.020.085.0220.325.0820.045.0160.4415.112.03.020.485.1219.484.8720.965.2460.9215.23合计81.3220.3380.0420.0178.6419.6624060.002.3.2 特深冲带钢规格数量分配(总产量60万吨)表2.7特深冲带钢规格数量分配表 万吨/年带钢厚度(mm)所占比例带钢宽度（mm）所占比例600900900150015002000合计万吨%万吨%万吨%万吨%0.50.84.701.1755.501.3755.301.32515.503.8750.81.25.401.354.801.204.201.0514.403.601.22.04.601.155.001.255.501.37515.103.7752.03.05.301.3254.701.1755.001.2515.003.75合计20.005.0020.004.5020.004.5060152.3.3 热镀锌带钢规格数量分配(总产量40万吨)表2.8 热镀锌带钢规格数量分配表 万吨/年带钢厚度(mm)所占比例带钢宽度（mm）所占比例600800800160016001800合计万吨%万吨%万吨%万吨%0.50.83.900.9753.840.963.480.8711.222.8050.81.23.600.902.760.693.520.889.882.471.22.02.860.7153.680.922.580.6459.122.282.03.02.640.663.720.933.420.8559.782.445合计13.03.2514.03.513.03.2540102.3.4 电镀锌带钢规格数量分配(总产量32万吨) 表2.9电镀锌带钢规格数量分配表 万吨/年带钢厚度(mm)所占比例带钢宽度（mm）所占比例500800800100010001100合计万吨%万吨%万吨%万吨%1.51.82.510.62752.550.63752.520.637.581.8951.82.22.540.6353.480.872.540.6358.562.1402.23.02.450.61252.510.62752.460.6157.421.8553.03.52.500.6253.460.8652.480.628.442.110合计10.02.5012.03.0010.02.5032.082.3.5 涂层带钢规格数量分配(总产量28万吨) 表2.10涂层带钢规格数量分配表 万吨/年带钢厚度(mm)所占比例带钢宽度（mm）所占比例600800800100010001100合计万吨%万吨%万吨%万吨%1.51.82.240.563.180.7952.020.5057.441.861.82.22.260.5652.320.582.040.516.621.6552.23.03.240.812.160.542.060.5157.461.8653.03.52.260.5652.340.5851.880.476.481.62合计10.02.510.02.58.02.028.073 轧制工艺流程及轧制制度的制定3.1 轧制工艺流程图热轧带钢仓库酸洗再结晶退火热镀锌冷轧产品特深冲产品清洗拉伸矫直电镀锌平整热镀锌产品再处理电镀锌产品清洗和预处理平整平整涂塑料或漆涂层产品冷轧横剪纵剪检查重卷3.2 各部分工艺流程3.2.1 带钢连续加工处理机组带钢连续加工处理机组是整个冷轧带钢的基本机组，它包括带卷的进料和出料、开卷机和卷曲机、焊接机、活套机组和张力和制动辊装置。设计时，应从工艺上考虑和确定机组的组成及设备布置和操作。带卷的进料和出料是依靠链式运输机，因为链式运输机在使用过程中只需要对链轮进行润滑的保养，不需要其它额外措施保养，节省了投资。开卷机和卷曲机采用液压控制，优点为占地面积小、重量轻。并且可以直接传动能量，有曲柄紧锁装置，适用于加减速大的快速轧机。传动性能的特点是飞轮力矩小，即使停止运行时间较长，也能使带钢保持恒定的张力轧制。卷筒采用双次液压涨缩控制，卷曲机卷筒布置楔块，目的是防止带卷内圈檫伤或变形。为了使机组的工艺段连续，在机组的开卷段设置焊接机，本机组采用闪光连续焊接机。活套机组采用带液压传动的活套小车并加装S辊装置的活套塔，其优点是占用空间小和充套容量大，易于控制带钢运行和带钢张力。活套塔前的S辊装置必须保证：当机组卷曲段或开卷段中的带卷停止运行时，仍使活套塔内原有的张力保持不变。通过S辊旁的夹紧辊实现此要求。薄带钢轧制时，保持恒定张力是机组正常运行的重要前提，因此加装了张力辊和制动辊装置(由称S辊)和被驱动的转向辊。除以上基本装置之外，带钢在高速运行时还会产生跑偏现象，因此要采用自动对中效能的圆柱形辊面。还包括：调节带钢应力的防跑偏装置是加一个摆动辊；侧向移动带钢运行平面的防跑偏装置是由一个或一对辊子组成，辊子设在一个旋转座上，旋转座可绕中心旋转；分卷穿带机组的防跑偏装置是设置可绕两个轴摆动的辊。主要的工艺流程为：带卷进料开卷夹持焊接进活套中间过程进活套飞剪卷曲(中间过程包括酸洗、带钢连续退火炉、带钢镀锌等)3.2.2 酸洗-冷轧联合机组酸洗-冷轧联合机组的选取是要根据所要求的生产能力、带钢宽度和带卷尺寸以及所采用的酸洗剂情况进行选择。本车间酸洗机组采用水平式浅槽紊流盐酸酸洗机组，原因是浅槽紊流盐酸酸洗具有酸洗带钢质量好、易于操作、作业率高、设备质量轻、投资少、消耗低、无公害等优点。其盐酸再生副产品-优质氧化铁粉纯度高、颗粒细、活性好，可为电子工业部门提供国内短缺的铁氧体磁性材料。清除带钢表面氧化铁皮的方法很多，最常用的是水平式（卧式）硫酸酸洗和盐酸酸洗。两者比较，盐酸酸洗具有产品质量好、生产能力高、金属和酸的损失少、成本低的优点。鲁兹那盐酸浅槽酸洗与传统的深槽相比具有以下优点：1.采用张力装置，带钢保持明显的张力，无自由悬垂活套，这意味着带钢在酸槽内总长度增加，从而增加了带钢的酸洗时间。2.测量和控制带钢垂度的问题没有了。3.出口侧张力辊（后S辊）仅仅是控制速度，入口侧张力辊（前S辊）则控制张力，从而简化了电气设备。4.停产时间酸洗液靠重力排入酸洗槽下面的贮酸容器内只需很短时间。断带时带钢段头易于寻找，而且便于处理，还可防止过酸洗。5.不需昂贵和精度较高的带钢提升装置。6.酸槽钢结构可减轻60%左右。7.可提高酸洗效率。8.具有酸洗特殊钢的能力。连续卧式酸洗机组之所以被称为连续的，是因为带钢连续的通过盛有酸溶液的酸洗槽。为了使过程连续，将后一卷带钢的端头与前一卷带钢的尾端焊接起来，再从酸洗槽通过，为下一步冷轧打下基础。连续酸洗机组可分为3段，分别为头部、中部、尾部。其中上料、拆卷、破碎带钢表面氧化铁皮、矫直、切头切尾、焊接、光整为原料准备段；拉矫、酸洗、漂洗、烘干为酸洗工艺段；剪边、涂油为酸洗成品段。整个机组的操作过程是：被送到机组的带钢卷，经过带有弯曲辊、给料装置和矫直机的开卷机将带钢端头拆开、矫直并被送入侧刀剪切掉带钢头尾，再将切完头尾的带钢闪光对焊机，将前后两条带钢的端头焊接起来，焊接处的焊缝通过焊机自身的光整机进行光整，然后拉料辊将带钢送入头部活套中贮存，以备酸洗工艺段生产。贮存在头部活套内的带钢由拉料辊拉出，并被连续的送入酸洗槽进行连续的酸洗。酸洗后清除掉氧化铁皮的钢板在漂洗槽中经高压水冲洗、毛刷刷洗除去带钢自酸洗槽中带出的残酸，再进入烘干装置将带钢表面烘干，然后送入圆盘剪进行剪边。本车间采用的全连轧机具有高产、优质、高效率和低耗等优点，其主要关键技术是：1.确保焊缝性能，轧制断带率低（小于2.5%），焊接工艺自动控制。焊缝自动探测，检测精度高。精确的焊缝跟踪和钢卷头尾及位置跟踪。2.在轧制中动态规格变换，变换段长度为4750mm（四五机架之间距）。3.带钢在300m/min飞剪分段，张力波动很小并快速导向。 4.带钢贮存装置，活套贮量大 。5.板形在线检测和计算机闭环控制。6.带钢留在机架中快速换辊。7.CVC轧辊凸度连续变化技术。生产过程全盘自动化，过程控制最佳化。具体的工作流程为：开卷矫直切头焊接和缝合加前张力活套装置加后张力酸洗冷水喷洗钝化热水漂洗带钢烘干加张力切边入口活套五机架四辊冷轧机圆盘剪剪切卷曲43.2.3 单垛式紧卷罩式退火机组在罩式退火炉中，一般将若干个紧卷的带卷叠为一垛成批加热，退火数小时后在进行冷却。紧卷的温升很慢。带卷中心达到给定温度要比带卷外圈迟很多。所以加热时间必须很长，直至中心部位也达到给定温度。经过长时间的退火，带钢组织变软，所以特别适合于深冲。具体的工艺流程为：带卷与垫板(即所谓的对流器)堆放入炉罩圆筒形内罩喷吹保护气罩加热外罩风机鼓风吊走加热罩，加罩冷却罩(快速冷却)喷吹冷空气停喷保护气冷致室温3.2.4 连续热镀锌机组冷轧带钢在镀锌前往往必须进行再结晶退火，以便在镀锌后保证基体金属具有所要求的工艺性能，如抗拉强度和可成型性。此外，还要将带钢表面上的所有残渣和杂质清洗掉。本车间采用的是一条大型、高速的带钢连续热镀锌机组，年生产能力在40万吨左右，工艺段最大速度达200m/min。该机组的技术特点如下：1.带钢镀锌前采用森吉米尔工艺，使带钢表面清理和热处理一次完成，适应高速生产要求。2.电感应加热陶瓷锌锅，温度控制精确（±30C），使用寿命长约20年，并有低液位探测、过热和泄漏报警。3.处理设备为大型全立式炉，具有延长炉辊寿命、改善带钢质量和缩短机组长度等优点。电感应加热陶瓷锌锅，温度控制精确（±30C），使用寿命长约20年，并有低液位探测、过热和泄漏报警。4.配置光整机和拉伸弯曲矫直机，使带钢平坦、性能改善。光整机可同时更换上、下辊而不需剪断带钢。5.用科勒气刀控制锌层厚度控制效率高，并由NDS计算机系统进行在线锌层重量测定并自动调节，使锌层厚度均匀。6.全线生产过程采用计算机控制，自动化程度高。本流程采用森吉米尔工艺，具体的工艺流程为：冷轧预清洗退火涂溶剂冷却到镀锌温度镀锌冷却冲洗拉伸矫直锌锅中的锌液温度为430450°C,正常运转的带钢温度为470510°C，辊身通常采用耐热合金钢，一般其化学成分为Co: 0.2%0.5%, Si: <2%，Mn: 2.0%, Ni: 10%14%, Cr: 20%24%, S: 0.04%。3.2.5 连续电镀锌机组与热镀锌相比，若不经过特殊的处理，电镀锌薄板呈暗灰色，锌层较薄，带钢每面的锌层厚度最大为5微米。电镀锌需要电解液进行处理，其成分见下表表3.1 带钢镀锌电解液成分含锌量85100克/升硫酸铵(NH4)2SO42530克/升pH值45电解液温度50 0C阴极电流密度达20安/分米2阴极电流效率100%电镀锌带钢具有锌层厚度均匀和表面光洁无锌花质量特征，特别适合做涂层基板，因而在汽车、家电、建材和轻工等部门得到十分广泛的应用。本机组采用不溶性阳极喷射式电镀工艺，生产双面镀锌、单面镀锌和差厚镀锌产品，并可进行磷化、钝化和涂油后处理。具有以下工艺特点：1.电镀槽卧式布置，采用小直径导电辊和电镀液喷流循环，可获得较高的电流密度，提高电镀速度，并易于切换到单面镀锌生产。2.带钢边缘有边缘罩，从而改善了边缘锌层增厚的现象，并可提高单面镀锌产品质量。3.使用不溶性阳极（Pn-Sn合金），使阳极和带钢表面比较清洁，镀层厚度均匀，阳极寿命期限为23年，更换不影响生产。4.电镀液以均匀流量反方向流经带钢表面，并且镀液浓度可自动调节，容易获得均匀的锌层。具体的工艺流程为：矫直开卷剪切焊接活套碱性电解清洗冲洗、刷洗酸洗冲洗、刷洗镀锌冲洗、刷洗冷水喷洗冲洗、刷洗磷酸盐处理冲洗铬酸盐处理烘干活套矫直检查3.2.6 涂层机组本车间采用的是二涂二烘工艺的高速带钢连续涂层机组。涂层带钢具有轻质、美观和良好的防腐性能等特点，而且可弯曲、冲压直接加工，是一种高附加值的新型材料，广泛应用于建筑、运输、家电家庭用品等制造行业。该机组的主要特点是：1.涂层设备为摆门式结构的辊涂机，可快速更换涂料和涂敷辊，使机组生产时间明显增加。2.工艺段速度高（146m/min），产品品种多，规格范围广，是一条多功能涂层机组。3.带钢预处理采用喷淋和浸渍方式进行强化预清洗，可使用冷轧和热轧带钢做基板。4.涂层厚度精度高，涂层厚度为2.5200m，重量误差为±5%。5.烘烤炉内配备温度测量和防爆监测控制系统，有焚烧炉和废热锅炉，即可充分利用热能，又可防止环境污染。6.生产过程计算机控制，自动化程度高。 工艺流程为：原料开卷平整校指切头焊接热碱水冲洗热水冲洗吹干活套热碱水冲洗刷洗热碱水冲洗热水冲洗磷化处理热水冲洗钝化处理吹干初涂初涂层烘干固化空气冷却水冷吹干精涂精涂层烘干固化空气冷却水冷吹干活套涂蜡卷曲3.2.7 薄板横剪机组和包装机组薄板横剪机组的布置应根据对成品薄板的品种要求，经济的剪切大量钢材，并按交货规格堆垛打包。根据以上要求，横剪机组的具体设备布置形式为：带卷输送和开卷装置夹送辊组或预矫直机及带钢矫直机带碎边剪的剪边机废边卷曲机带钢测厚装置横剪机17辊薄板矫直机21辊薄板矫直机分类台打印机涂油机一极品堆垛机涂油机输出辊道磅秤 涂油机二极品堆垛机具体工艺流程为：开卷夹持矫直剪切废边卷曲测厚横剪17辊矫直21辊矫直涂油，打印堆垛称量包装的任务就是把堆成垛的钢板和卷成带的钢卷捆紧，以保证安全运输。另外，应当根据用户规定或根据不同的钢板品种、单张板材规格、运输和存库条件，保证防损伤、防污染和防锈。本流程设计的钢板包装方法是：在每个操作台设有一条独立传动的运输链。向板垛下供纸、复盖钢板和包装钢带的供送都是自动进行。相应的垫木台运输链结构，能够很好的将木料按纵木横木，以及横木下钉纵木方式垫好，垫木台设有液压升降装置，用它才能在横木下垫放纵木。带卷的包装采用绕捆机。3.2.8 连续辊压成形机组（备选）连续辊压成形机组用来把冷轧、热镀锌和涂层带钢连续辊压成形为建筑、交通运输等工业需用的梯形波纹板，成形深度为38mm和75mm两种（最大130mm），连续成形，机组主要特点为：1.电动随动剪自动定尺连续剪切，剪切质量好。2.设置红外线烘烤装置，保证冷天辊压涂层钢板无裂纹缺陷5。3.3轧制制度的制定3.3.1 压下规程的制定典型产品为Q345，规格为1.2mm1280mm，来料规格为3.5mm1350mm。表3.2 宽度允许偏差公称宽度/mm允许偏差/mm高精度一般精度<1200+2+300>1200+6+600表3.3 基板镰刀弯允许最大值种类镰刀弯最大值/mm 测量长度/mm钢板0.003×公称长度公称长度钢带525003.3.2 计算各道轧制压下的步骤说明各机架摩擦系数的选取：第一道次考虑咬入，不喷油，故取0.08，以后喷乳化液，取值在0.050.06之间，具体值见下表。表3.4 摩擦系数表1#轧机2#轧机3#轧机4#轧机5#轧机0.080.050.050.050.05本设计采用M